| Fabrication of CoFe/BaFe12O19 magnetic nanocomposite thin films by electrodeposition |
| Paper ID : 2306-UFGNSM13-FULL |
| Authors: |
| Abstract: |
| A study of the incorporation of barium hexaferrite nanoparticles into a CoFe matrix by means of electrodeposition over brass substrates has been performed. Barium hexaferrite nanoparticles were prepared by co-precipitation route using solution of iron and barium nitrates with a Fe3+/Ba2+molar ratio of 8, by addition of NaOH with a OH-/NO3- molar ratio of 2. X-ray diffraction (XRD) results indicated that in a sample synthesized from aqueous solution and annealed at 900 C for 1 hour, BaFe12O19 was the dominant phase. Field emission scanning electron microscopy (FE-SEM) showed plate-like particles of barium hexaferrite by mean diameter of 300 nm and thickness of 45 nm. CoFe-BaFe12O19 nanocomposite thin films were then electrodeposited froma Co-Fe bath containing the barium hexaferrite particles obtained in the first stage of this work. Finally, FE-SEM equipped with energy dispersive spectroscopy (EDS) analyzer and XRD analysis was applied on the deposited films, to confirm presence of the nanoparticles in the film. The average crystallite size of the deposits was around 30 nm. It was also noticed that increasing the concentration of the particles in the electroplating bath, caused a rise in the BaFe12O19 content of the deposits but had no significant effect on the composition of the CoFe matrix. |
| Keywords: |
| magnetic thin films, nanocomposite, electrodeposition, CoFe alloy, barium hexaferrite |
| Status : Paper Accepted (Poster Presentation) |
© 2010 - 2024 All Rights Reserved. Powered by sinaweb.